Pibellau dur aloi ferritig di-dor ASTM A335

Dec 04, 2025

Beth yw pibellau dur aloi ferritig di-dor ASTM A335

ASTM A335/ASME SA335 Uchel-Pibau Dur Alloy Ferritig Di-dor Tymhereddyn{0}}bibellau dur perfformiad uchel sy'n dangos ‌cryfder ymgripiad tymheredd uchel rhagorol, bywyd gwasanaeth uchel tymheredd uchel, a gwrthiant ocsidiad tymheredd uchel uwch. Maent yn gwrthsefyll pwysau o dan dymheredd uchel tra'n cynnal digon o gryfder a chadernid i ‌sicrhau diogelwch system a gweithrediad sefydlog‌.

Mae manylebau a dimensiynau ‌ASTM A335/ASME SA335 Uchel-Pibau Dur Alloy Ferritig Di-dor TymhereddGellir ei addasu yn unol â gofynion cais penodol. Yn gyffredinol, mae'r pibellau hyn yn cynnwys ‌ystod diamedr allanol o 21.3 mm i 762 mmac aystod trwch wal o 3.0 mm i 130 mm‌.

‌ASTM A335/ASME SA335 Uchel-Pibau Dur Alloy Ferritig Di-dor Tymhereddyn cael eu defnyddio'n eang mewn systemau pibellau tymheredd uchel ar draws diwydiannau petrolewm, cemegol a phŵer oherwydd eu ‌ymwrthedd tymheredd uchel eithriadol a phriodweddau mecanyddol dibynadwy. Er enghraifft, maent yn gwasanaethu fel deunyddiau gweithgynhyrchu ar gyfer:

-tymheredd uchel, -piblinellau pwysedd uchel, adweithyddion, a chyfnewidwyr gwres yn ‌purfeydd olew a phlanhigion cemegol‌;

Cydrannau hanfodol fel ‌superheaters boeler, ailgynheswyr, a phibellau stêmmewn gorsafoedd pŵer thermol.

Cyfansoddiad Cemegol:

Gradd	CU Sequiv.	C Llai na neu'n hafal i	Mn	P Llai na neu hafal i	S Llai na neu'n hafal i	Si Llai na neu hafal i	Cr	Mo
P1	K11522	0.10~0.20	0.30~0.80	0.025	0.025	0.10~0.50	–	0.44~0.65
P2	K11547	0.10~0.20	0.30~0.61	0.025	0.025	0.10~0.30	0.50~0.81	0.44~0.65
P5	K41545	0.15	0.30~0.60	0.025	0.025	0.5	4.00~6.00	0.44~0.65
P5b	K51545	0.15	0.30~0.60	0.025	0.025	1.00~2.00	4.00~6.00	0.44~0.65
P5c	K41245	0.12	0.30~0.60	0.025	0.025	0.5	4.00~6.00	0.44~0.65
P9	S50400	0.15	0.30~0.60	0.025	0.025	0.50~1.00	8.00~10.00	0.44~0.65
P11	K11597	0.05~0.15	0.30~0.61	0.025	0.025	0.50~1.00	1.00~1.50	0.44~0.65
P12	K11562	0.05~0.15	0.30~0.60	0.025	0.025	0.5	0.80~1.25	0.44~0.65
P15	K11578	0.05~0.15	0.30~0.60	0.025	0.025	1.15~1.65	–	0.44~0.65
P21	K31545	0.05~0.15	0.30~0.60	0.025	0.025	0.5	2.65~3.35	0.80~1.60
P22	K21590	0.05~0.15	0.30~0.60	0.025	0.025	0.5	1.90~2.60	0.87~1.13
P91	K91560	0.08~0.12	0.30~0.60	0.02	0.01	0.20~0.50	8.00~9.50	0.85~1.05
P92	K92460	0.07~0.13	0.30~0.60	0.02	0.01	0.5	8.50~9.50	0.30~0.60

Gofynion Tynnol

Cryfder Tynnol, min., psi	P-5	P-9	P-11	P-22	P-91
ksi	60	60	60	60	85
MPa	415	415	415	415	585
Yield Nerth, min., psi
ksi	30	30	30	30	60
MPa	205	205	205	205	415

Priodweddau Mecanyddol

Priodweddau mecanyddol	P1,P2	P12	P23	P91	P92,P11	P122
Cryfder tynnol	380	415	510	585	620	620
Cryfder cynnyrch	205	220	400	415	440	400

Gofynion Triniaeth Gwres

Gradd	Math Triniaeth Gwres Ll5, P9, P11, a P22	Normaleiddio Ystod Tymheredd F [C]	Anelio neu Dirwest Isfeirniadol Amrediad Tymheredd F [C]
A335 P5 (b,c)	Aneliad Llawn neu Isothermol
	Normaleiddio a Thymer	*****	1250 [675]
	Anneal Subcritical (P5c yn unig)	*****	1325 – 1375 [715 - 745]
A335 P9	Aneliad Llawn neu Isothermol
	Normaleiddio a Thymer	*****	1250 [675]
A335 P11	Aneliad Llawn neu Isothermol
	Normaleiddio a Thymer	*****	1200 [650]
A335 P22	Aneliad Llawn neu Isothermol
	Normaleiddio a Thymer	*****	1250 [675]
A335 P91	Normaleiddio a Thymer	1900-1975 [1040 - 1080]	1350-1470 [730 - 800]
	Torri a Thymer	1900-1975 [1040 - 1080]	1350-1470 [730 - 800]