Beth yw deunydd SA 335 P12
Jan 06, 2026
Mae SA335 P12 yn bibell ddur aloi molybdenwm cromiwm o dan y safon ASTM, gyda chyfansoddiad cemegol o 1Cr-0.5Mo (C<0.15%, Cr0.8-1.25%, Mo0.44-0.65%). Its high-temperature strength is significantly improved through the solid solution strengthening effect of aluminum. Compared to ordinary 20G boiler tubes, its creep strength at 540°C is increased by approximately 40%, and the allowable stress can reach 78MPa (ASME standard). This material must simultaneously meet the triple standards of ASTM A335 (materials), A213 (cold drawing), and A370 (mechanical testing), and must undergo 100% eddy current testing and hydraulic testing (test pressure >60MPa) cyn gadael y ffatri.
Manyleb
Mae pibellau dur P12 fel arfer ar gael mewn meintiau sy'n amrywio o 25-762mm mewn diamedr a 3-50mm mewn trwch wal.
Technolegau Allweddol yn y Broses Gynhyrchu
Mae cynhyrchu pibellau dur SA335 P12 o ansawdd uchel yn gofyn am reolaeth dros dair agwedd graidd:
1. Mae'r broses fwyndoddi yn defnyddio proses driphlyg EAFLFVD, gan reoli cynnwys sylffwr a ffosfforws i Llai na neu'n hafal i 0.015% a chynnwys hydrogen i Llai na neu'n hafal i 2ppm;
2. Mae rholio poeth yn defnyddio proses dreigl a reolir mewn dau gam, gyda'r tymheredd treigl terfynol yn cael ei reoli ar 880 ±20 gradd i sicrhau ailgrisialu austenit cyflawn;
3. Rhaid i driniaeth wres gadw at drefn normaleiddio (900-930 gradd) a thymheru (680-730 gradd), gan arwain at ficrostrwythur bainite tymherus unffurf.
Ceisiadau
Mewn unedau boeler supercritical, defnyddir pibellau dur P12 yn bennaf yn:
Uwch-gynhesyddion tymheredd isel (tymheredd wal Llai na neu'n hafal i 450 gradd )
Penawdau economizer
Prif systemau cymorth pibellau stêm
SA335 P12 tymheredd uchel aloi ffatri bibell